Suitable for protruding and fillet welding (downward and lateral). Capable of high-efficiency welding construction. Slag volume is about the same as that of solid wire.
Product Type | Welding Wire | Wire Diameter(mm) | 1.4 | Current range, lower(A) | 80~400 |
---|---|---|---|---|---|
Current range, vertical position, elevating, upper | 70~180 | JIS Standards | Z3313 T 49J 0 T15-1 C A-R (Previously YFW-C50DM) | AWS Standards | A5.18 E70C-6C, A5.18 E70C-6M |
Compatible Material Type | For Sheet | Internal Capacity | 1 Box (20 kg) | Mass(g) | 20000 |
Applications and use properties | Thin plate butt-jointing and fillet weld, pipe initial layer penetration welding. Capable of short arc welding. Arc is stabilized by low current, making it suitable for thin plate. Compared to solid wire, it is durable against burn-through, and can easily handle thin plates of around 0.8 mm. Amount of slug is equivalent to solid. | Main point of operation | Can also use mixed gas (AR+CO2). | Chemical Composition C for Weld Metal(%) | 0.08 |
Chemical Composition Si for Weld Metal(%) | 0.49 | Chemical Composition Mn for Weld Metal(%) | 1.53 | Chemical Composition P for Weld Metal(%) | 0.013 |
Chemical Composition S for Weld Metal(%) | 0.013 | Mechanical Properties of The Weld Metal - Proof Stress Mpa | 479 | Mechanical Properties of The Weld Metal - Proof Stress Tensile Strength Mpa | 559 |
Mechanical Properties of The Weld Metal - Proof Stress Extension(%) | 26 | Mechanical Properties of The Weld Metal - Proof Stress Absorption Energy(J) | 99 |