Excellent impact resistance and glass transparency. *Quoted from Takiron plate comprehensive catalog 2013.
[Features]
· Polycarbonate plate is a material with excellent impact-resistance among plastic materials.
· Plastic with a transparency equal to glass that refutes the common belief that transparent materials are easy to break.
· Possesses among the highest level of impact-resistance strength while using transparent materials with approximately 20 times the strength of rigid PVC and approximately 40 times the strength of acrylic.
· Superior light permeability rate of 85% or more for 5 mm transparent plate, the same transparency as high grade plate glass.
· Low thermal conductivity (1/5th of glass) and superior heat retention qualities. Useful for insulation effect.
· Can be used in a wide range of practical operating temperatures from -40°C to +120°C.
· 1 mm in thickness and resistant to high voltages of up to 30,000 volts. More than twice the insulating value as phenol-formaldehyde resin and best suited as electric insulation material.
· Weather-resistant grade that prevents yellowing and is barely affected by direct sunlight, wind, rain and temperatures, when compared to other plastic materials. Quality can be selected based on application.
· The Food Sanitation Act of Japan / UL certified product / railway car compliant certified product.
[Processing features of polycarbonate]
1. Little change in load (creep) and easy drilling and cutting.
2. Vacuum forming and heat bending possible.
3. Cold forming by bending into a curve under temperatures below room temperature is possible.
Item evaluated | Unit | PC1600 | ||
---|---|---|---|---|
Physical Properties | Specific Gravity | — | 1.20 | |
Rockwell Hardness | M scale | 67 | ||
R scale | 125 | |||
Mechanical Properties | Tensile yield stress | MPa | 63 | |
Nominal strain at break | % | 90 | ||
Tensile elasticity | MPa | 2250 | ||
Notched Charpy impact strength | kJ/m^2 | 13.0 | ||
Tensile impact strength | kJ/m^2 | 220 | ||
Bending stress | MPa | 91 | ||
Bending Elasticity Ratio | MPa | 2300 | ||
Compressive yield stress | MPa | 78 | ||
Compressive Modulus | MPa | 1900 | ||
Shear fracture stress | MPa | 65 | ||
Thermal Properties | Deflection Temp. Under Load | °C | 0.45 MPa | — |
°C | 1.80 MPa | 139 | ||
Vicat Softening Temperature | °C | Method A (10 N) | — | |
°C | Method B (50 N) | 150 | ||
Heat distortion rate | % | Vertical | ※3 3.5 | |
lateral | ※3 -0.2 | |||
Linear expansion coefficient | × 10-5·K-1 | 6.5 | ||
Thermal conductivity | W/m·K | 0.19 | ||
Specific Heat | J/g·K | 1.30 | ||
Flame Resistance | — | — | ||
Electrical Properties | Surface Resistivity | ohms per square | 10^15 or more | |
Volume resistivity | Ω・m | 10^13 or more | ||
Dielectric strength | MV/m | 20 | ||
Permittivity (1 MHz) | — | 3 | ||
Dielectric loss tangent (1 MHz) | — | 0.009 | ||
— | Laminating properties | — | — | |
Moisture Absorption | % | 0.240 | ||
Optical Properties | Total light transmission | % | 89 | |
Haze | — | — | ||
Hue | — | Transparent |
* The indicated values are actual measured values for a test piece with a thickness of 5 mm, and are not guaranteed values.
Test condition 190°C / 60 minutes (tested according to JIS K 6735)
Part Number |
---|
L-PC1600-2-[1201-2000/1]-[20-1000/1] |
L-PC1600-2-[1201-2000/1]-[20-1000/1] |
L-PC1600-3-[1201-2000/1]-[20-1000/1] |
L-PC1600-3-[1201-2000/1]-[20-1000/1] |
L-PC1600-5-[1201-2000/1]-[20-1000/1] |
L-PC1600-5-[1201-2000/1]-[20-1000/1] |
PC1600-2-[20-1200/1]-[20-1000/1] |
PC1600-2-[20-1200/1]-[20-1000/1] |
PC1600-3-[20-1200/1]-[20-1000/1] |
PC1600-3-[20-1200/1]-[20-1000/1] |
PC1600-5-[20-1200/1]-[20-1000/1] |
PC1600-5-[20-1200/1]-[20-1000/1] |
Part Number | Price | Name | Minimum Order Qty. | Volume Discount | Days to Ship | Plate Thickness (mm) | Length (mm) | Width (mm) |
---|---|---|---|---|---|---|---|---|
- | TKR NONMETAL SHEET | 1 Piece(s) | 5 Day(s) | 2 | 20 ~ 1000 | 1201 ~ 2000 | ||
- | POLYCARBONATE PLATE | 1 Piece(s) | 7 Day(s) | 2 | 20 ~ 1000 | 1201 ~ 2000 | ||
- | TKR NONMETAL SHEET | 1 Piece(s) | 5 Day(s) | 3 | 20 ~ 1000 | 1201 ~ 2000 | ||
- | POLYCARBONATE PLATE | 1 Piece(s) | 7 Day(s) | 3 | 20 ~ 1000 | 1201 ~ 2000 | ||
- | TKR NONMETAL SHEET | 1 Piece(s) | 5 Day(s) | 5 | 20 ~ 1000 | 1201 ~ 2000 | ||
- | POLYCARBONATE PLATE | 1 Piece(s) | 7 Day(s) | 5 | 20 ~ 1000 | 1201 ~ 2000 | ||
- | TKR NONMETAL SHEET | 1 Piece(s) | 5 Day(s) | 2 | 20 ~ 1000 | 20 ~ 1200 | ||
- | POLYCARBONATE PLATE | 1 Piece(s) | 9 Day(s) | 2 | 20 ~ 1000 | 20 ~ 1200 | ||
- | TKR NONMETAL SHEET | 1 Piece(s) | 5 Day(s) | 3 | 20 ~ 1000 | 20 ~ 1200 | ||
- | POLYCARBONATE PLATE | 1 Piece(s) | 7 Day(s) | 3 | 20 ~ 1000 | 20 ~ 1200 | ||
- | TKR NONMETAL SHEET | 1 Piece(s) | 5 Day(s) | 5 | 20 ~ 1000 | 20 ~ 1200 | ||
- | POLYCARBONATE PLATE | 1 Piece(s) | 7 Day(s) | 5 | 20 ~ 1000 | 20 ~ 1200 |
Loading...
Material | Polycarbonate (PC) | Color | Transparency | Grade | Standard |
---|---|---|---|---|---|
Hole Machining | No Hole Machining |
How can we improve?
How can we improve?